http://ipicyt.repositorioinstitucional.mx/jspui/handle/1010/2484| On the synthesis, structural transformation and magnetocaloric behavior of Ni37.5Co12.5Mn35Ti15 melt-spun ribbons | |
| MAURICIO LOPEZ CRUZ JONATHAN ZAMORA MENDIETA CESAR FIDEL SANCHEZ VALDES JOSE LUIS SANCHEZ LLAMAZARES | |
| Acceso Abierto | |
| Atribución-NoComercial-SinDerivadas | |
| https://doi.org/10.1063/9.0000163 | |
| Martensitic-transformation | |
| "We fabricated Ni37.5Co12.5Mn35Ti15 melt-spun ribbons at linear wheel speeds (WS) of 20 and 8 ms(-1) (series A and B, respectively). The effect of a short time thermal annealing (30 min.) between 1023 K and 1173 K on the martensitic-like structural transition and the crystal structure, microstructure and magnetic entropy change Delta S-M(T) curves and related parameters for as-solidified (AS) samples of series A were studied. Whereas the Curie temperature of austenite (AST) T-C(A) keeps nearly constant, both the reduction of the solidification rate and the increase on the thermal annealing temperature increase the temperature of the structural transformation reducing the magnetization change across the AST to martensite (MST) transition. The martensitic transformation (MT) in AS samples undergoes from a B2-type ferromagnetic (FM) AST with T-C(A) = 328 K to a monoclinic martensite (MST); SEM images evidenced a partially grain-oriented microstructure formed by columnar in shape-elongated grains with their major axis oriented along the thermal gradient during solidification. Magneto-structural transition for AS ribbons of series A occurs in the vicinity of room temperature and is accompanied by a magnetization change of around 63 Am(2)kg(-1). For a magnetic field change of 2 T these samples showed a maximum magnetic entropy change |Delta S-M|(max) of 13.8 (9.5) J kg(-1) K-1 for the MST -> AST (AST -> MST) transformation. This is below the previously reported for this alloy composition (27.2 J kg(-1) K-1), and is related to the broader magneto-structural transition." | |
| American Institute of Physics | |
| 2021 | |
| Artículo | |
| M. López-Cruz, J. Zamora, C. F. Sánchez-Valdés, and J. L. Sánchez Llamazares, "On the synthesis, structural transformation and magnetocaloric behavior of Ni37.5Co12.5Mn35Ti15 melt-spun ribbons", AIP Advances 11, 015010 (2021); https://doi.org/10.1063/9.0000163 | |
| CIENCIAS TECNOLÓGICAS | |
| Versión publicada | |
| publishedVersion - Versión publicada | |
| Aparece en las colecciones: | Publicaciones Científicas Nanociencias y Materiales |
Cargar archivos:
| Fichero | Tamaño | Formato | |
|---|---|---|---|
| AIPAdvances11(2021)015010.pdf | 5.27 MB | Adobe PDF | Visualizar/Abrir |